1. Product Features

1. Can effectively control the ratio of anode to cathode.

2. The anode has good solubility and produces less anode slime.

3. Convenient loading or supplement of anode material.

4. The anode material is completely used, saving energy consumption.

5. The characteristics of titanium-clad copper: it can not only ensure the original conductivity of the copper material, but also use titanium to protect the copper body from corrosion, and greatly reduce

In addition to electroplating, the contamination of electroplating solution.

2. How to use

1. poor conductivity of titanium, typically the hook out of the water flowing current is not more than 0.26A ² , otherwise the hook body heat, resulting in a plating solution temperature rises high, the amount of cooling increases, waste of energy, because the heat will burn even plastic tank It is found that when the titanium basket hook becomes significantly hot, the number of titanium baskets or the cross-sectional size of the titanium basket hook can be increased to improve the conductivity of the titanium basket.

2. Titanium blue hook and electrode generally do not use flat or round surface contact, this method is easy to cause poor contact, causing spot corrosion of the electrode.

3. The titanium basket opening should be slightly above the liquid level to prevent the outflow of anode slag.

4. The lower end of the titanium basket should be 100-150mm higher than the parts to avoid excessive concentration of current in the lower parts and cause scorching.

5. The titanium basket should be in close contact with the anode, otherwise the anode potential on the titanium basket will rise sharply, causing oxygen evolution and chlorine evolution reactions on the surface of the titanium blue, causing damage to the titanium blue and oxidation of the additives.

6. In order to prevent burrs in the coating, the anode bag should be wrapped in the titanium basket, because the bag is usually used for a long time without removal, so it is recommended to use the "double bag" method.

7. The anode bag should wrap the titanium basket tightly, and a gap of a few centimeters should be left at the bottom of the bag to store the anode sludge that may be generated.